Property
|
Test
Method
|
Performance
|
| Weight
Per YD2 |
ASTM
D 1910 |
12
oz. |
| Nominal
Thickness (mils) |
|
24
Mils |
Tensile
Strength
(Grab Method) |
ASTM
D 751 |
WARP
449 LBS.
WEFT 405 LBS. |
| Elongation
to Break |
|
WARP
29%
WEFT 34% |
Tear
Strength
(Tongue Method) |
ASTM
D 751 |
WARP
74 LBS/IN.
WEFT 94 LBS/IN. |
Bursting
Strength
(Diaphragm Method) |
ASTM
D 751 |
812
PSI |
| Hydrostatic
Resistance |
ASTM
D 751A |
310
PSI |
Puncture
Resistance
(1" Steel Ball Tipped Probe) |
ASTM
D 751 |
642
PSI |
| Moisture
Vapor Transmission |
ASTM
E96 B |
0.4647
GRAMS/M2/24HRS |
| Low
Temperature Cold Crack |
ASTM
D 2136 |
-65°F |
| Flex/Abrasion |
ASTM
D 3885 |
No
damage to scrim after 2800 cycles, black coating worn
away. |
Dimensional
Stability
@ 212F/1HR |
ASTM
D 1204 |
@Edge:
WARP -9.3
WEFT -7.7
@Center:
WARP -7.6
WEFT -6.4 |
| Accelerated
Weathering, UV |
ASTM
G 53 |
More
than 80% of strength retained after 2000 hours. |
| Carbon
Black Content |
|
2% |
| Carbon
Black Dispersion |
|
A-1 |